摘要
Widegapbrazing(WGB)experimentsusingthebuttedspecimenwitha1.5mmgapwerecarriedoutfortherepairofthefailedK418Bsuperalloylow-pressureturbinevanes.Thehightemperaturecreeprupturestrengthsofthebrazedjointsweretested,andthemicrostructuresandfracturesurfacesofthejointswereobserved.TheresultsshowthatthemicrostructureofK418Balloyjointiscomposedofdenseequiaxedgrain,smallanddiscretecompoundswithafewmicro-pores.Duringthecreeprupturetest,thecracksinitiatepreferentiallyatthemicro-poreorthegrainboundary,thenpropagatealongthegrainboundarytillthefracturehappens.Thecreeprupturestrengthat700℃ofthebrazedjointswith50%brazemetalintheworkingpartcouldexceed90%thatoftheK418Bsuperalloy,andthejointswith100%brazemetalintheworkingpartachieve70%to80%ofthecreeprupturestrengthsfortheK418Bbasemetal.
出版日期
2016年04月14日（中国期刊网平台首次上网日期，不代表论文的发表时间）