简介:利用同步辐射(BSRF)漫散射站四圆衍射仪,对SiC体单晶的结构进行了判定以及对利用常压化学气相沉积(APCVD)生长的3C-SiC/Si(001)中的孪晶及含量进行了分析。六方{10-15}极图证明了该SiC单晶为6H(H为Hexagonal的缩写)结构。对3C-SiC外延薄膜,Φ扫描证明了3C-SiC外延生长于Si衬底上,外延取向关系为:(001)3C-SiC//(001)Si,[111]3C-SiC//[111]Si。3C-SiC的{111}极图在x=15.8°出现了新的衍射,采用六方{10-10}极图以及基体倒格点111、孪晶倒格点002的Mapping分析了x=15.8°处产生的衍射为3C-SiC孪晶所致,并利用ω扫描估算了孪晶的含量约为1%。
简介:<正>“Privacy”istranslatedasyinsiinChinese.Traditionally,intheChinesemind,yinsiisassociatedwithsomethingthatisclosedorunfair.Ifsomeoneissaidtohaveyinsi,meddlers(好事者)willbeattractedtopry(打探)intohisorheraffairs.Sopeoplealwaysstatethattheydon’thaveyinsi.
简介:TheinvestigationonopticalpropertiesofSi1-xGex/Sistrainedlayerstructureshasbeencarriedoutactivelyinrecentyears.Thephotoluminescencehasbe-comeabriskersubjectinthestudiesofitsvariousopticalproperties.Aresearchdevelop-menttophotoluminescencepropertiesofsomenewSi1-xGex/Sistrainedlayerstruc-turesisintroduced.
简介:Theresidualelectricallyactivedefectsin(4×1012cm-2(30KeV)+5×1012cm-2(130KeV))si-implantedLECundopedsi-GaAsactivatedbytwo-steprapidthermalannealing(RTA)LABELEDAS970℃(9S)+750℃(12S)havebeeninvestigatedwithdeepleveltransientspec-troscopy(DLTS).TwoelectrontrapsET1(Ec-0.53eV,σn=2.3×10-16cm2)andET2(Ec-0.81eV,σn=9.7×10(-13)cm2)aredetected.Furthermore,thenoticeablevariationsoftrap’scon-centrationandenergylevelintheforbiddengapwiththedepthprofileofdefectsinducedbyionim-plantationandRTAprocesshavealsobeenobserved.The[Asi·VAs·AsGa]and[VAs·Asi·VGa·AsGa]areproposedtobethepossibleatomicconfigurationsofET1andET2,respectivelytoexplaintheirRTAbehaviors.
简介:PhotoconductivityCharacteristicsofPorousSi①CHAOZhanyun,WANGKaiyuan(DepartmentofElectronicEnginering,SoutheastUniversity,Nanji...
简介:PitformationandsurfacemorphologicalevolutioninSi(001)homoepitaxyareinvestigatedbyusingscanningtunnelingmicroscopy.Anti-phaseboundaryisfoundtogiverisetoinitialgenerationofpitsboundbybunchedDBsteps.Theterracesbreakupandarereducedtoacriticalnucleussizewithpitformation.Duetoanisotropickinetics,adownhillbiasdiffusioncurrent,whichislargeralongthedimerrowsthroughthecentreareaoftheterracethanthroughtheareaclosetotheedge,leadstotheprevalenceofpitsboundby{101}facets.Subsequentannealingresultsinashapetransitionfrom{101}-facetedpitstomulti-facetedpits.
简介:研究Al-Mg-Si合金晶界组成相(Al-Mg2Si及Al-Mg2Si-Si)间的电化学行为和动态电化学耦合行为,提出Al-Mg-Si合金的晶间腐蚀机理。研究表明,晶界Si的电位比其边缘Al基体的正,在整个腐蚀过程中作为阴极导致其边缘Al基体的阳极溶解;晶界Mg2Si的电位比其边缘Al基体的负,在腐蚀初期作为阳极发生阳极溶解,然而由于Mg2Si中活性较高的元素Mg的优先溶解,不活泼元素Si的富集,致使Mg2Si电位正移,甚至与其边缘Al基体发生极性转换,导致其边缘Al基体的阳极溶解。当n(Mg)/n(Si)〈1.73时,随着腐蚀的进行,合金晶界同时会有Mg2Si析出相和Si粒子,腐蚀首先萌生于Mg2Si相和Si边缘的无沉淀带,而后,Si粒子一方面导致其边缘无沉淀带严重的阳极溶解,另一方面加速Mg2Si和晶界无沉淀带的极性转换,从而促使腐蚀沿晶界Si粒子及Mg2Si粒子边缘向无沉淀带发展。
简介:莫斯科钢与合金研究所利用机械一化学合成法成功合成一种特殊的准单晶物质,在工业领域有广泛应用前景。在这种物质中,铁、铜、铝三种原子的排列不像普通单晶那样具有相同的晶格,但仍具有严格的顺序,呈现出几何排列。以橡胶和聚合物为底基,辅以这种准单晶物质制成的复合材料具有金属和陶瓷的双重特性,像金刚石一样坚硬,摩擦系数小于金属,化学稳定性和耐摩性很高。
简介:摘要本文从埚转、等径功率、投料量等几个方面论述了直拉硅单晶中氧含量的控制方法,通过工艺调整,降低硅单晶的氧含量,改善晶体品质。