简介：Inthiswork,thewettability,agingandshearpropertiesofanewtypeoflead-freesolderpasteSn-07Ag-05Cu+BiNi(SACBN07)wasinvestigatedbyconductingaseriesofcomparisonexperimentswithSAC305andSAC0307solderpaste.TheresultsshowthatwettabilityofSACBN07isalmostequaltoSAC305,andbetterthanthatofSAC0307solderpaste.Thethicknessofintermetalliccompound(IMC)layerinSACBN07/Cuislowerthanthatofothertwotypesofsolderjointafteraging.AndCu_3SnlayerofSACBN07/CuisthinnerthanthatofSAC305andSAC0307.Inaddition,theSACBN07solderjointsperformthebestshearstrengthamongthesethreetypesofsolderpastes.

简介：WeldingresearchofA6N01S-T5aluminumalloyprofileforhigh-speedtrainwasdonebyusinglaser-MIGhybridweldingandMIGweldingindividually.Andtheweldappearance,weldingdistortion,mechanicalpropertiesofthejointsandmicrostructureswereanalyzed.Thetestresultsdemonstratedthathigh-efficientweldingfortheprofilecanbeachievedbyusinglaser-MIGhybridwelding,thespeedofwhichcanbeover3.0m/min.Theprocessinghadagoodgapbridgingability，evenifthegapofthebuttjointwasupto2.0mm,agoodweldappearancecanalsobegot.Whilethehybridweldingspeedwasgreaterthan2.5m/min,theweldingdistortionofthelaser-tandemMIGhybridjointswasjustabout33%ofthatoftheMIGjoints,buttheweldingefficiencywasover3timesofMIGwelding.Andtensilestrengthofthehybridjointswas85%ofthatofA6N01S-T5basemetal,9%higherthanthatoftheMIGjoints.Fatiguepropertieswastestedindividuallywithpulsedtensilefatiguemethodintheconditionof1×107lifetime.Thetestresultsdemonstratedthatthefatiguestrengthofthejointswasalittlelowerthanthatofbasematerial,whichcouldbeupto115MPa.Butthefatiguestrengthofhybridweldingjointswas107.5MPa,whichwas23%higherthan87MPaofMIGweldingjoints.

简介：FlameheatingcombinedwithwatercoolingwasusedtostraightenA6N01aluminumalloyweldedjointandeffectofflameheatingpassonitsmicrostructureandmechanicalpropertieswasstudied.ResultsshowedthattheflameinducedtheprecipitationandgrowthoftheMg2SiphaseontheAlsubstrateforthethermalagingA6N01aluminumalloyweldedjoints,thusitledthedecreaseofmicro-hardnessandtensilestrengthoftheA6N01aluminumalloyweldedjointwiththeincreaseoftheheatingpass.However,thefatiguepropertyoftheflameheatedjointwasimprovedbecausetheMg2Siprecipitationhinderedtheinitiationandpropagationofthefatiguecrack.