简介：ThecorrelationbetweenphasestructuresandsurfaceacidityofAl2O3supportscalcinedatdifferenttemperaturesandthecatalyticperformanceofNi/Al2O3catalystsintheproductionofsyntheticnaturalgas(SNG)viaCOmethanationwassystematicallyinvestigated.Aseriesof10wt%NiO/Al2O3catalystswerepreparedbytheconventionalimpregnationmethod,andthephasestructuresandsurfaceacidityofAl2O3supportswereadjustedbycalciningthecommercialγ-Al2O3atdifferenttemperatures(600–1200C).COmethanationreactionwascarriedoutinthetemperaturerangeof300–600Catdifferentweighthourlyspacevelocities(WHSV=30000and120000mL·g-1h-1)andpressures(0.1and3.0MPa).ItwasfoundthathighcalcinationtemperaturenotonlyledtothegrowthinNiparticlesize,butalsoweakenedtheinteractionbetweenNinanoparticlesandAl2O3supportsduetotherapiddecreaseofthespecificsurfaceareaandacidityofAl2O3supports.Interestingly,NicatalystssupportedonAl2O3calcinedat1200C(Ni/Al2O3-1200)exhibitedthebestcatalyticactivityforCOmethanationunderdifferentreactionconditions.LifetimereactiontestsalsoindicatedthatNi/Al2O3-1200wasthemostactiveandstablecatalystcomparedwiththeotherthreecatalysts,whosesupportswerecalcinedatlowertemperatures(600,800and1000C).ThesefindingswouldthereforebehelpfultodevelopNi/Al2O3methanationcatalystforSNGproduction.

简介：A60%Fe/Al2O3catalystwaspreparedbytheco-precipitationmethod.ItwasreducedbyH2toproducemetallicFe,whichwasthensulfidedbyCS2toFe0.96SandFe3S4orphosphidedbytriphenylphosphine(PPh3)inliquidphasestoFe2PandFeP.Itwasfoundthattheironsulfides(Fe0.96SandFe3S4)exhibitedthelowactivityforthehydrodesulfurization(HDS)reactions.TheHDSactivitywasalsolowontheFe(metal)/Al2O3andFe2P/Al2O3catalystssincetheywereconvertedintoFe0.96SandFe3S4duringtheHDSreactions.Incontrast,theFeP/Al2O3wasfoundtobestableandactivefortheHDSreactions.Inparticular,FeP/Al2O3possessedsignificantlysmallerFePparticlesthanFeP/C,leadingtothesignificanthigherHDSactivityofFeP/Al2O3thanFeP/C.

简介：Al2O3/Al的三个系列把陶器的矩阵composites，命名矿泉，SPV和HP压成薄片，被不同方法制作。矿泉和SPV经由屏幕在空或真空中打印和随后的热处理用Al2O3片和艾尔泥浆被准备。HP样品被热压成为艾尔陪衬和Al2O3片的分层的栈。SEM和XRD被使用分析微观结构和夹层水晶阶段。弯曲力量，破裂坚韧和三个方法做的样品的破裂工作被测量并且比较。结果证明composites比Al2O3片有好一些的坚韧和更高的破裂工作。在三个方法做的样品之中，热压做的样品有最佳机械性能。排水量负担曲线和骨折机制被分析。

简介：HotcompressionbehaviorofTiC–Al2O3/AlcompositeswasstudiedusingtheGleeble-1500systematatemperaturerangeof300–550°Candatstrainraterangeof0.01–10.00s-1.TheassociatedstructuralchangeswerestudiedbyTEMobservations.Theresultsshowthatstressleveldecreaseswithdeformationtemperatureincreasingandstrainratedecreasing,whichcanberepresentedbyaZener–Hollomonparameterinanexponent-typeequationwithhotdeformationactivationenergyQof172.56kJ·mol-1.Dynamicrecoveryoccurseasilywhenstrainratesarelessthan10.00s-1.Dynamicrecrystallizationcanoccuratstrainrateof10.00s-1.

简介：

简介：

简介：TheinteractionbetweenZn-AleutecticalloyandAl2O3p/6061Alcompositesinthevacuumfurnacewasinvestigated.Greatattentionhasbeenpaidtotheelementsdiffusion,themicrostructureandformationoftheinterfacebetweenZn-AIeutecticalloyandAl2O3p/6061Alcomposites.ExperimentalresultsshowthatZn-AleutecticalloyhasagoodwettingabilitytoAl2O3p/6061Alcompositesandthewettingangledecreaseswithincreasingthetemperatureinvacuum.Aftertheinteraction,aninteractionlayerformsbetweenZn-AIalloyandAl2O3p/6061Alcomposites.Thephasesintheinteractionlayermainlyconsistofα-Al(Zn),Al2O3andCuZn5resultedfromthediffusionofelementsfromtheZn-Alalloy.SeveralporositiesdistributeintheregionneartheinterfaceoftheZn-Alalloy/interactionlayer.TheamountofshrinkagevoidsintheinteractinglayerisrelevanttothepenetrationofZnelementintoAl2O3p/6061Alcompositeswhichisafunctionoftemperature.SoitisnecessarytolowerheatingtemperatureinordertolimittheZnpenetration.

简介：BondingofAl2O3tocuisperformeddirectlyusingTifoilattemperatureof1273K.Themicrostructureofthejointinterfaceisinuestigatedthroughscanningelectronmicroscope（SEM）,electron.probemicroanalysis（EPMA）andX-raydiffraction（XRD）.theeffectoftheinitialtifoilthicknessonthereactionlayerthicknessandthejointStrengthareinvestigated.

简介：用固体碱[Mg（Al）O]负载金属氧化物（Co2O3）作催化剂，在常压下催化分子氧氧化正丁硫醇向二硫化物转化。实验考察了镁铝摩尔比、催化剂焙烧温度及活性组分钴含量与催化剂活性的关系，还考察了反应温度和溶剂对正丁硫醇氧化反应的影响。结果表明，Co2O3／Mg（Al）O具有较好的催化活性和稳定性。在镁铝摩尔比3：1、Co含量8％、活化温度600℃条件下制得的催化剂活性最好。常压下用Co2O3／Mg（Al）O催化分子氧氧化正丁硫醇的适宜反应条件为：甲醇作溶剂，反应温度40℃。用IR、UV对正丁硫醇的氧化产物的结构进行了表征。

简介：

简介：

简介：以超重力场辅助燃烧合成技术制备了呈梯度分布的Y2O3-Al2O3-SiO2玻璃／Y3Al5O12陶瓷梯度复合材料。结果表明，梯度布置两种组分的原料既可防止下层熔体的喷溅，又能提高上层玻璃的透过率。该梯度材料沿超重力方向依次为YAS透明玻璃层、YAS-YAG玻璃陶瓷层和YAG陶瓷层。

简介：Siliconcarbide(SiC)-alumina(Al_2O_3)-mullite(Al_6Si_2O_(13))compositepowderwassuccessfullysynthesizedat1550℃for5hviacarbothermalreductionreaction,andtheeffectsofvariousmassratiosofactivecarbontoflyash(0.38,0.44and0.58)onthephasecompositionandmicrostructureofproductswereinvestigated,andtheformationprocessofthepowderwasalsoanalyzedindetail.Theproductsmainlyconsistofβ-SiC,α-Al_2O_3,Al_6Si_2O_(13)andFeSi.IncreasingcarboncontentfavorsthedecompositionofAl_6Si_2O_(13)andformationofSiC.Theaverageparticlesizeofβ-SiCandα-Al_2O_3isabout1μmandthatofAl_6Si_2O_(13)is5-10μm.TheformationprocessofSiC-Al_2O_3-Al_6Si_2O_(13)powderincludesthedecompositionofmulliteinflyashandformationofSiC.

简介：0.5%Pt-K/γ-Al2O3catalystsforthesynthesisofo-phenylphenol(OPP)fromo-cyclohexenyl-cyclohexanone(dimer)dehydrogenationwerepreparedbymeansofatwosubsequentimpregnationmethod.Theeffectsofcatalystpreparationparameters,suchasKpromoters,calcination,andreductionconditions,wereinvestigated.TheresultsshowedthattheadditionofK2SO4toPt/γ-Al2O3catalystnotablypromotedtheselectivityofOPP,anditsoptimumcontentwasfoundtobe6%inmassfraction.ThehigheractivitywasobtainedwhenPt/γ-Al2O3catalystwascalcinedinnitrogenatmosphereat400―500°Candthenreducedatthesametemperaturefor3hinhydrogenatmosphere.TheconversionofthedimerandtheselectivityofOPPwerealwaysabove99%and90%,respectively,over0.5%Pt-6%K2SO4/γ-Al2O3catalystduringthepilotscaletestof8000h.

简介：Themicrostructureandslagerosionfractaldimensionofreactioninterfaceofβ-Sialon-Al2O3brickusedin300MtironladleofBaosteelhavebeenstudiedbySEMandXRD.Theresultsindicatedthatβ-Sialon-Al2O3brickexhibitedexcellentslagresistance.Themainwearmechanismofβ-Sialon-Al2O3brickismainlyfromthespallingcausedbythermalmechanicalstressandattackedbyslagsecondly.

简介：Al2O3-MgOcastableshavebeenwidelyusedforworkingliningsofsteelladleduetotheirsuperiorhotstrengthandcorrosionresistance.Inthiswork,effectsofmicrosilica,ultrafinealuminaandMgOfinesadditionsontherheologicalbehaviorofthecastableswereinvestigatedbymeansofIBBrheometerV1.0tomeasuretorque(shearstress)undervaryingshearrates.Theresultsshowthatrheologicalpropertiesofcastablesatvaryingshearratesaresignificantlyimprovedwithincreaseofmicrosilicaadditions(from1mass%to5mass%)andcorrespondingdecreaseinwateraddition;thereisonlylittlechangeinrheologicalbehaviorwithvariationofultrafinealuminaandMgOfinesadditions.Optimumultrafinealuminaandmicrosilicaadditionsarerecommendedforcastableswithgoodrheologicalbehavior.

简介：

简介：Thecorrosionbehaviorandanti-corrosionmechanismoftheZn-Ni-Al2O3compositecoatingwereinvestigatedbySEM,EDSandXPS.TheresultsindicatethatthecorrosiontypeoftheZn-Ni-Al2O3coatingsinneutral5wt.%NaClsolutionisuniformcorrosion.ThepresenceofcompactanduniformlydispersednanoaluminaparticlessubstantiallyinhibitsthecorrosionofZn-Ni-Al2O3compositecoatings.Intheinitialcorrosionstage,thecorrosiveproductsofZn-NimatrixformacompactZnCl2·4Zn(OH)2layer.Withthedevelopmentofcorrosion,somenanoaluminaparticlesareembeddedandformaNienrichmentlayer.InNienrichmentlayer,NipresentsasNiandNiO.

简介：

简介：TheinfluencesoffourkindsofadditivesaddedintothematrixofMgO-Al2O3unbunedproductswereinvestigated,TheresultsshowthatsampleswithproperMgO/Al2O3rationandproperadditionofCr2O3(2%-4%)havegoodthermalshockresistanceandslagcorrosionresistanceaswell,XRDandSEMdeterminationresultsindicatethatakindofcompoundspinel(Mg,Al,Cr)O4wasformedandthemicrostuctureofthesamplesaredenser.