简介:研究热挤压Al5083/B4C纳米复合材料的显微组织表征和力学行为。Al5083和Al5083/B4C粉末在氩气气氛和旋转速度400r/min条件下球磨50h。为提高伸长率,将球磨粉末与30%和50%(质量分数)平均粒径>100μm和<100μm未球磨粉末进行混合,然后进行热压和热挤压,挤压比为9:1。采用光学显微镜、扫描电子显微镜、能谱、透射电子显微镜、拉伸和硬度测试研究了热挤压合金。结果表明,机械球磨和B4C颗粒使Al5083合金的屈服强度从130MPa提高至560MPa,但伸长率急剧下降(从11.3%降至0.49%)。添加平均粒径<100μm未球磨颗粒可提高合金的塑性但降低拉伸强度和硬度,而添加平均粒径>100μm未球磨颗粒同时降低拉伸强度和塑性。随着未球磨颗粒含量的增加,断裂机理从脆性断裂转变为韧性断裂。
简介:ThemixturemodelofAl85Y4Nd4Ni7alloyinwhichapartiallycrystallizedamorphousalloyisregardedasananocompositeofanAlnanoparticleandaremainingamorphousmatrixispresented.Itsevolutionintheprocessofcrystallizationhasbeeninvestigatedbydifferentialscanningcalorimetry(DSC),X-raydiffraction(XRD),andtransmissionelectronmicroscopy(TEM).Mainlyamorphousstructurewithα-Alnanocrystalsembeddedintheamorphousmatrixhasbeenrevealedbymeltspiningthealloy.Crystallizationisshowedtooccurinthreestages:(1)crystallizationofamorphousalloyandformationofAlNiY,AlNdNiandunknowncrystallinephases,(2)formationofAl3YandAl3Nd,and(3)formationofAl3Ni.
简介:运用循环伏安法、线性电位扫描法研究木糖醇在碱性溶液(含锑)中的电化学稳定性及锑在木糖醇碱性溶液中的沉积动力学参数;采用计时电流法研究锑在不锈钢阴极上的电化学成核机理。循环伏安测试结果表明,木糖醇在碱性溶液中的稳定性较好,在-1.20V~+0.60V(vsHg/HgO)范围内无氧化还原反应发生,在电位负于-1.70V(vs.Hg/HgO)时木糖醇在锑电极上可能发生分解。在该体系中,锑在阴极上的沉积经历了不可逆电结晶过程。根据线性电势扫描结果,锑沉积的活化能、表观传递系数、交换电流密度等动力学参数分别为46.33kJ/mol、0.64和4.40×10-6A/m2。计时电流法实验结果表明,锑在碱性木糖醇溶液中的成核机理符合扩散控制下的三维连续成核模型,外加电位对晶体生长速率和恒定电位下的饱和晶核密度有显著影响。通过分析恒电位阶跃曲线,求出锑离子在该体系中的扩散系数为1.53×10-6cm2/s。
简介:Non-stoichiometriccompoundfluoride-dopedLiFePO4/Ccathodematerialsweresynthesizedviasolid-statereactionusingMgF2andAlF3asdopant.Thefluoride-dopedLiFePO4/CsampleswerecharacterizedbyX-raydiffraction(XRD),scanningelectronmicroscopy(SEM),transmissionelectronmicroscopy(TEM),andelectrochemicaltesting.TheresultsshowthatthematerialsarewellcrystallizedandfluoridedopingcannotchangethespacestructureofLiFePO4.SlightamountsofFe2O3withnofluorideimpuritywere...
简介:Inthiswork,asimpleandfacileone-potoleylaminesolvothermalsyntheticmethodwasdevelopedtosynthesizeCu_2ZnSnS_4(CZTS)nanocrystals.AndtheCu_2ZnSn(S,Se)_4(CZTSSe)thinfilmswerepreparedbyselenizingCZTSnanocrystals.TheobtainedCZTSnanocrystalsandCZTSSefilmswerestudiedusingX-raydiffraction(XRD),transmissionelectronmicroscopy(TEM),scanningelectronmicroscopy(SEM),energy-dispersiveX-rayspectroscopy(EDX),andultraviolet–visiblespectrophotometer(UV–Vis).TEMresultsshowthatthesphere–likeCZTSnanoparticleswithdiameterbetween12and35nmarepolydispersed.XRDstudiesindicatethatthepreparedCZTSnanocrystalsformkesteritecrystalstructure,andtheCZTSSefilmswithkesteritecrystalstructurearealsoobtainedattheannealingtemperaturesof500and550°C.Inparticularafterannealingat500°Cfor20min,theCZTSSefilmexhibitsasmooth,uniform,crack-free,andlarge-grainedtopographyandpossessesCu-poorandSn-richcomposition.Moreover,itshowsstrongopticalabsorptionfromvisibletonear-infrared(IR)region,anditsopticalbandgap(Eg)isfoundtobeabout1.44eV.
简介:本文采用双酚A环氧树脂和高导热性无机填料制作了一种高导热型铝基覆铜箔层压板。该产品性能稳定.基本可以达到国外同类产品技术指标。